In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

Galvanized barbed wire as a safety protection of the metal wall, the galvanized barbed wire device also need to be protected for a long time? And how to protect it? Maintenance and protection of galvanized barbed rope. First, we can start from two aspects. One is about the protection of galvanized barbed rope posts.

Because zinc layer corrosion resistance, can be applied to all kinds of environment, use is also very convenient, has been more popular hardware products. Galvanized iron wire should pay special attention to the acyl washing, to slowly put into the container, to prevent acid sputtering on the body, and prohibit the water into the water, so that it is easy to let the acid out, to learn to handle gently, stacking should also be firm and neat. It can be widely used in architecture, handicrafts and other daily civilian applications.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

Heavy hexagonal net, also known as large size hexagonal net, or gabion mesh, made of steel wire by twisting mesh machine. This product is very versatile. Can be used for slope support, foundation pit support, mountain rock surface hanging net shotcrete, slope planting (greening), railway highway isolation barrier, it can also be made of stone cage, stone pad, for rivers, DAMS and seawall anti-erosion protection and reservoirs, river interception with stone cage.

After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance. There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, electric power transmission, shipbuilding and other industries.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

Stainless steel blade barbed wire production process is similar to galvanized blade barbed wire production process, usually according to the mold to determine the size of the blade.

The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.

Galvanized hook mesh standard is thorough, mesh planning: 3cm-20cm, silk planning: 1.2mm-4.5mm, galvanized hook mesh 6000 square meters, some standards are available. Benefits: The selection of low carbon steel wire, surface for cold galvanized (electric galvanized) hot dip galvanized anticorrosion treatment, mesh wire strong, strong protection, long anticorrosion time.