This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

Under any application environment, users hope that the welding mesh has better strength, as long as it has improved in strength, it will make better use of the demand, but to make the strength of this product improve, also need to have many conditions, to see what kind of data manufacturers have in production, the strength of the product is the strength of the data, But a manufacturer does not meet the strength requirements in the data, and naturally, it cannot make the strength of the product improve after all, so this is the condition.

Hot dip galvanizing is then oiled and chromed. The quality of hot-galvanized sheet produced by this method is significantly improved compared with that by wet galvanizing method. It is only valuable for small-scale production. Continuous galvanizing production line includes a series of pretreatment procedures, such as alkali degreasing, hydrochloric acid pickling, water washing, solvent coating, drying, etc., and the original plate needs to be annealed in cover furnace before entering the galvanizing line.

The barbed rope factory not only provides the sales work of blade barbed rope, including the subsequent construction, but also contracted together, and the construction price is particularly different.

First of all, we need to pay attention to the material of the barbed wire, because the galvanized barbed wire itself includes cold plating and hot plating. The properties and prices of the two are obviously different, and it is easy to be confused by a little negligence.

Annealing wire is widely used mainly because it has a good elasticity and flexibility, in the annealing process can be a good control of its hardness and softness, it is mainly made of iron wire, more commonly used in the construction industry tie wire use. When the wire factory is in production, the annealing wire will be processed according to the performance of the material, and its hardness will be changed according to the different demand, which can make it have more advantages, reduce the consumption of metal and reduce the cost of production.

Although galvanized iron wire has the protection of galvanized layer, it does not say that it will not rust at all, but delays the time of rust. In general, cold galvanized iron wire can be kept for 1-2 years without rust, hot galvanized iron wire can be used for 8-10 years without rust. If properly maintained, the use time will be longer. So how to prevent galvanized iron wire rust?

Galvanized hook net cost is low: galvanized process is faster than other coating construction method, and can avoid the installation of time required on the site brushing; Galvanized hook net features: not easy to corrosion, long life, strong practicality, uniform mesh, smooth net surface, simple weaving, beautiful and generous, high quality mesh, wide mesh, thick wire diameter. Can do breeding protection net, coal mine protection net, court protection net, stadium fence net, training field protection net, slope protection, green enclosure, river, building, residential district safety protection, workshop/warehouse isolation, etc..

Galvanizing is a process of coating a metal surface with zinc in an electrochemical reaction on the metal surface to improve the corrosion resistance of the metal. Wire drawing is a process in which metal materials are drawn by mechanical methods to reduce their cross-sectional area and increase their length. So, the combination of galvanized to wire drawing two processes, what impact on the performance of the product?

The advantage of galvanized iron wire after annealing: after annealing increases the elongation of the iron wire. Makes the product softer and increases the range of application. After electric galvanizing hot dip galvanizing. Copper electroplating is widely used and screen production. Galvanized iron wire is a soft iron wire product processed by low carbon steel wire through cold drawing, heating, constant temperature, and even heat preservation. Generally, the quality of ordinary galvanized iron wire will be relatively soft, the softness is relatively balanced, and the color is consistent. It is mainly used in construction, mining, chemical industry and so on.

Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.