The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.

Welding mesh is widely used in industry, agriculture, breeding, construction, transportation, mining and other aspects. Such as machine shields, animal fences, flower fences, window fences, access fences, poultry cages, egg baskets and home office food baskets, paper baskets and decorative. We can make it according to the special requirements of customers. Welding mesh is made of high quality low carbon steel wire row welding, and then cold plating (electroplating), hot plating, PVC plastic coated surface passivation, plasticizing treatment, smooth mesh, uniform mesh, solid solder joint, local machining stable performance, corrosion resistance, corrosion resistance. Features: Stainless steel mesh selection of high quality stainless steel wire row welding, more acid, alkali resistance, solid welding, beautiful, widely used and so on.

This oxide film has greater elasticity and lubricity, does not affect the accuracy of parts. Therefore, the parts of precision instruments and optical instruments, spring steel, thin steel sheet, fine steel wire and so on are commonly bluing treatment. The commonly used galvanizing treatment of large roll galvanized wire is equivalent to forming a protective layer on the surface of the iron wire. The commonly used methods are hot dip galvanizing, hot spray plating, vacuum plating and so on. Different methods have corresponding characteristics.

In view of this situation, many manufacturers are committed to ensuring the corrosion resistance of titanium and titanium alloy under the premise of increasing the hardness of titanium alloy, and surface carburizing is one of the typical processing technology means. Similar to the surface carburizing treatment of steel, the surface carburizing treatment of titanium alloy is to make the active carbon atoms, diffusion to the internal of titanium alloy, the formation of a certain thickness of higher carbon content of the carburizing layer, after quenching and tempering, so that the surface layer of the workpiece to obtain high carbon content of titanium alloy wire.

Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.

2, the production and installation is simple and fast, the use of patented friction connection or special connection accessories for installation, greatly improve the installation efficiency.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

5, after the light plating should be carried out light treatment.