Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.

2, galvanized wire mesh molding sheet storage ground should be flat, according to the symbolic requirements of the accumulation of regular, height should not exceed 2M, and away from heat sources, avoid exposure.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

This process has no mold, low processing cost, easy forming, can process a variety of shapes and other characteristics are widely used. But the products of the guardrail are powder impregnated plastic. According to whether it needs heating, it is divided into hot dipping and cold dipping. According to the raw materials of dipping, it can be divided into liquid dipping and powder dipping. Hot-dip galvanizing, as a metal anticorrosion method, is usually to put the steel structure to be derusted into the zinc liquid at about 500℃, so that the zinc layer is attached to the surface of the steel structure.

Galvanized iron wire can be divided into hot-dip galvanized iron wire and cold galvanized iron wire according to different processing methods. Galvanized iron wire is more prominent in its corrosion resistance. Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Galvanized iron wire products are widely used in construction, handicrafts, wire mesh preparation, the production of galvanized hook mesh, wall mesh, highway guardrail, product packaging and daily civilian and other fields.

Because the coastline is generally erected for protection, but often because of environmental factors lead to serious corrosion of the barbed rope lost its function. Stainless steel barbed rope is specially set up to prevent corrosion. Stainless steel barbed rope because the environmental requirements are not very high can be very good protection itself will not have a problem to extend the use of life, so that you can ensure safety.

The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.