Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries, in the agricultural field such as pesticide irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

In use, there is no need for daily maintenance and maintenance, not only can save a lot of time, but also can reduce costs, but also has good stability, strong corrosion resistance, greatly prolong the service life. According to the different process is divided into different types, can choose according to their own needs. With good flexibility and elasticity, the main role of annealing wire is to control its degree of softness and hardness, in the production of annealing wire is made of steel wire, now more used in the construction industry binding use, compared with ordinary wire is also more soft, have better luster.

The application of electric welding mesh is more widely, at present, it has replaced the use of other parts of the screen, the cost of electric welding mesh is low, the production speed is very fast, so it is very popular. The treatment required before galvanized welding mesh is recrystallization annealing, because the welding mesh must maintain an oxide and no other impurities of pure iron active surface, if you can’t keep its surface clean will lead to poor galvanized effect, galvanized layer and iron material is not tightly combined, so this step is necessary.

Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.

Under any application environment, users hope that the welding mesh has better strength, as long as it has improved in strength, it will make better use of the demand, but to make the strength of this product improve, also need to have many conditions, to see what kind of data manufacturers have in production, the strength of the product is the strength of the data, But a manufacturer does not meet the strength requirements in the data, and naturally, it cannot make the strength of the product improve after all, so this is the condition.

Each coil of steel wire shall consist of one wire. The surface of the rod shall not have cracks, folds, scars, ears, layers or inclusions. However, indentation, pits, bumps, scratches and pockmarks are allowed, and the depth or height shall not be 0.2mm. There should be no corrosion and oxidation skin on the surface of the steel wire, and oxidation color is allowed by heat treatment. The surface of the wire is allowed to have scratches not exceeding half of the allowable deviation range of the diameter, and local defects not exceeding the allowable deviation of the appropriate diameter.

Because the coastline is generally erected for protection, but often because of environmental factors lead to serious corrosion of the barbed rope lost its function. Stainless steel barbed rope is specially set up to prevent corrosion. Stainless steel barbed rope because the environmental requirements are not very high can be very good protection itself will not have a problem to extend the use of life, so that you can ensure safety.

Electric galvanized shaft wire direct selling is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanizing shiny white.

In general, the cost of hot dipping zinc is lower than that of other maintenance coatings. The reason is very simple. Other maintenance coatings, such as sand painting, are labor-intensive processes, whereas hot dipping zinc processes are highly mechanized and tightly controlled in-plant construction. Hot dip zinc coating can be visually and briefly tested for non-destructive coating thickness.