Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.

In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.

Large rolls of galvanized wire in oxygen violently extinguished, spark, and sodium block, magnesium strip in oxygen extinguished, no spark phenomenon. This phenomenon is determined by the composition of galvanized wire. The galvanized wire used in the experiment is pig iron or steel wire, pig iron and steel are iron and carbon alloy, containing iron and carbon two elements of complex material. Carbon in galvanized wire will produce carbon dioxide when extinguished, solid into gas, volume will shrink rapidly.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.