No matter how good the quality of hot-dip galvanized barbed rope is, it is only attached to the surface of the wire with galvanized layer, and with the cause of chemical reaction, the zinc layer on the surface will gradually lose its effect because of oxidation reaction, which is more prominent in the humid area of the environment. And because, after all, the wire will rust, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.

Stainless steel is short for rust acid steel, air, steam, water and other weak corrosion medium or stainless steel is called stainless steel; And the chemical corrosion resistance medium (acid, alkali, salt and other chemical etching) corrosion of steel called acid steel.

3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, filtration test, and then take a small amount of electroplating solution, with zinc powder treatment after the test, check the problem is solid particles or copper, lead and other foreign metal impurities caused by. One by one, it’s not hard to find the cause of the problem. Galvanized iron wire coating blister, poor adhesion.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

The cooling circulation system uses spray to cool the drawing die, and takes away a lot of heat generated by the drawing machine in high speed drawing in time to ensure the quality of the wire. Control drawing process parameters: drawing speed 10 ~ 12m/s; Winding tension 8 ~ 10N; Measuring length 30km; The mass fraction of lubricant is 3.5 ~ 4.5%; pH value of lubricant 7 ~ 8; Lubricant temperature 30 ~ 40℃.

In use, there is no need for daily maintenance and maintenance, not only can save a lot of time, but also can reduce costs, but also has good stability, strong corrosion resistance, greatly prolong the service life. According to the different process is divided into different types, can choose according to their own needs. With good flexibility and elasticity, the main role of annealing wire is to control its degree of softness and hardness, in the production of annealing wire is made of steel wire, now more used in the construction industry binding use, compared with ordinary wire is also more soft, have better luster.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.