The galvanizing process of galvanized wire products is a very effective metal anticorrosion method. It is also widely used in other industrial fields. The use of galvanized iron wire is very common in metal structure equipment of various industries. Due to the influence of production technology or other factors, the zinc layer of galvanized wire products will be different to a certain extent, especially ordinary galvanized can not reach the beauty of electric galvanized, the zinc layer of ordinary galvanized wire is mainly for corrosion prevention.

Construction welding net work wall insulation project using galvanized welding network in wall insulation and rust engineering project plays a necessary role, wall painting batch putty network is divided into two kinds: this is galvanized welding network; Another is to change the wire drawing wire welding mesh, according to the provisions of the region, construction enterprises to carry out effective material selection. Construction welded wire mesh new mink cage new mink cage grommet see more 1 inch, from silk in 2 mm up and down, management method is simple and easy, a mesh surface bright and clean and is not easy to scratch mink, galvanized welded wire online zinc quantity proportion, it is not easy to rust, new mink cage up more convenient, mink settled in natural environment more comfortable, the price also is higher than before the same specifications of the mink cage competitive many, But the overall character is not harmed at all, it is stronger.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

High-speed road guardrail net, hexagonal mesh of all kinds of guardrail net, the value of the high-speed road is more prominent, it is not only used in a variety of roads, in a variety of sports ball fields and landslides to take care of, but also to reach a very close utility.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.