The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

After proper heat treatment or cold drawing hardening, high carbon steel wire has high strength and hardness, high elastic limit and fatigue limit (especially notched fatigue limit), cutting function is acceptable, but welding function and cold plastic deformation ability is poor.

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Traditional barbed wire is crisscross woven into the wire, with the development of the economy, the rapid rise of all walks of life, the limitations of the use of traditional barbed wire gradually exposed, such as: aquaculture, to the chicken circle cage can not be too dense, the wire can not be too thick, woven mesh wire once the mesh will become soft. We also have coping methods: 1, cotton gouging, rolling straight wire into wavy shape, but still not enough to raise chickens with mesh can only be extended to the beak can not feed! 2, is the electric welding net, with the current of the longitude and weft wire spot welding together, the mesh is not limited to do more.

A. When the thickness of the plating is 3-4 mm, the zinc adhesion should be less than 460g/m, that is, the average thickness of the zinc layer is not less than 65 microns.

The first is the cost of raw materials galvanized sheet and galvanized wire, some specifications and waste calculation and so on. Then there is the cost of mechanical processing process and manual processing process. Finally, there is the cost of packing and shipping. In recent years, due to the rapid development of thorn rope manufacturers, so the profit margin of blade thorn rope is not particularly broad.