Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

Hot wire is made of high quality low carbon steel, high carbon steel, after drawing, hot galvanized processing galvanized wire. Hot dip galvanized wire production process: wire rod – drawing – annealing – drawing – annealing – galvanized. Hot dip galvanized wire has the characteristics of thick coating, strong corrosion resistance and solid coating. And according to the special needs of users, according to the industry standard to provide various specifications of galvanized wire. Hot-dip galvanized wire is of better quality than electrodip galvanized wire. In the production process, hot dip galvanized wire has more than one annealing process, so the corrosion resistance of hot dip galvanized wire is stronger than that of electric galvanized wire.

The different spacing of the thorn rope is mainly in order to save costs to consider, because if they are too close, then obviously a little waste of resources, but the installation is too sparse will not work. Usually the bottom spacing is about 10cm, and the top is up to 20cm, this is because the higher the place is more difficult to climb over, usually more than one meter without the help of tools it is difficult for ordinary people to climb over, and the bottom because of the relatively tight can prevent personnel from drilling in the past.

Galvanized wire mesh is divided into hot dip galvanized wire mesh and cold galvanized wire mesh. Galvanized steel wire net selects the high quality low carbon steel wire, iron wire factory made by precision of automation machinery welding technology processing, smooth surface, firm structure, integrity is strong, even if the local cutting of galvanized steel wire net, or local also under pressure from loose phenomenon, after molding, wire mesh galvanized corrosion resistance good, has the advantage that the general steel mesh does not have.

Stainless steel blade barbed rope material is produced according to stainless steel plate and stainless steel wire, as a whole have achieved the purpose of high quality anticorrosion.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

Take 20cm galvanized wire for acid fog experiment, check the zinc content of galvanized wire through the balance to see whether it meets the zinc layer standard required by customers, ensure that the metal wire achieves the role of rust and corrosion prevention, and meet the service life required by customers. Galvanized iron wires must be packed in good condition, bound neatly and orderly, and bound inward to prevent scratches during transportation. The inspection standard of galvanized iron wire also includes the tensile test, which is decided according to the material of the galvanized wire order ordered by the customer, and it needs to be tested by comparing the raw material list.

Galvanized iron wire will rust, mainly and the thickness of galvanized layer and the use of the environment, galvanized iron wire is also divided into cold galvanized iron wire and hot galvanized iron wire, in general, hot galvanized iron wire galvanized layer is thicker, rust prevention time is longer, generally can be 7 or 8 years without rust. If the galvanized layer is damaged, or long-term use in a humid environment, it will accelerate the rust time of galvanized iron wire.

Galvanized hook net cost is low: galvanized process is faster than other coating construction method, and can avoid the installation of time required on the site brushing; Galvanized hook net features: not easy to corrosion, long life, strong practicality, uniform mesh, smooth net surface, simple weaving, beautiful and generous, high quality mesh, wide mesh, thick wire diameter. Can do breeding protection net, coal mine protection net, court protection net, stadium fence net, training field protection net, slope protection, green enclosure, river, building, residential district safety protection, workshop/warehouse isolation, etc..