The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

Cold wire drawing is mainly used in the production of hardened low carbon steel wire, with a diameter of 8 mm steel bar to play a fixed role in the development of the construction industry has played a role in promoting the development of the construction industry, widely used. The bonding and anchorage performance between cold wire drawing and concrete is good. When used in components, the phenomenon of cracking in the anchorage area of components and damage caused by steel wire slip is fundamentally eliminated, and the bearing capacity and anti-cracking capacity of the end of components are improved.

Iron and steel in the condition of cooling on the surface galvanized, and hot dip galvanized steel pipe in the condition of hot dip on the surface, its adhesion is strong, not easy to fall off, hot dip galvanized pipe although also rust phenomenon, but in a long period can meet the technical and sanitary requirements.

Iron and steel in the condition of cooling on the surface galvanized, and hot dip galvanized steel pipe in the condition of hot dip on the surface, its adhesion is strong, not easy to fall off, hot dip galvanized pipe although also rust phenomenon, but in a long period can meet the technical and sanitary requirements.

Zinc is a silver-white metal, brittle at room temperature, soluble in acid and alkali, known as amphoteric metal. Pure zinc is more stable in dry air, and small in humid air or water containing carbon dioxide and oxygen. A thin film layer of basic zinc carbonate will be formed on the surface, which can delay the corrosion rate of zinc layer. The corrosion resistance of galvanized layer in aqueous solution of acid, alkali and sodium chloride is relatively strong. It is also not resistant to corrosion in atmospheres containing carbon dioxide and hydrogen sulfide and in Marine atmospheres; In high temperature and high humidity air and containing organic acid atmosphere is small, galvanized layer is also easy to be corroded.

Electric galvanized wire direct selling is in the plating tank through the current one-way to gradually zinc plating on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanizing shiny white.

Unless the stainless steel blade barbed rope is specially customized, it is usually produced by the mould with the knife length of 22mm, which is the BTO-22 type we usually call. This is not necessarily the specification from 11mm to 65mm are specifications. Unless the customer insists on customized length requirements, the barbed rope manufacturer will produce BTO-22 stainless steel blade barbed rope.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging treatment.

The large roll of galvanized silk should be coated with oil, the fiber core is dipped in oil, and the grease should be able to protect the fiber core from decay and corrosion, the iron wire moistens the fiber, and lubricates the wire rope from the inside. The surface is coated with oil so that all the wire surface in the rope strand is evenly coated with a layer of anti-rust lubricating grease, which is used for the mine rope with friction lifting and mineral water, to be coated with black grease with increased wear and strong water resistance. Other uses are coated with red oil oil with strong film and good rust resistance, and require it to have a thin oil layer, which is easy to keep clean during the operation.

What’s the difference between cold galvanized wire and hot galvanized wire? It is mainly different production process. Cold galvanized iron wire, also known as electric galvanized iron wire, is the use of electrolytic galvanizing process, and hot galvanized iron wire is the use of hot penetration galvanizing process. Compared with the two, hot dip galvanized iron wire thick coating, high zinc content, has stronger anti-corrosion and anti-rust effect. Similarly, the price is also higher, cold galvanized iron wire and hot galvanized iron wire which good? Mainly for the use of scenarios and requirements to choose appropriate galvanized iron wire, appropriate is better.

Wire-wall welding net is widely used in industrial production, agriculture, engineering construction, transportation, mining and other processing and manufacturing industries. Such as machinery and equipment protective cover, animal guardrail, pot flower guardrail, window fence, safety exit guardrail, poultry cage, egg basket and home office food industry basket, paper basket and design decoration. It is suitable for general engineering building wall, pouring concrete, multi-storey building, etc., which plays an important structural role in the thermal insulation system. In the construction of the building, the thermal insulation board of hot-dip galvanized electric welding grid is placed on the inside of the outer mold of the wall to be concreted. The external thermal insulation board and the wall are one kind of live, and the thermal insulation board and the wall are integrated into one body after the removal of the mold. The coating on the surface of the weld core is called the coating. The coating of electrode plays a very important role in the welding process. If the photoelectrode without drug skin is used for welding, in the welding process, oxygen and nitrogen in the air will invade a large number of molten metal, metal iron and beneficial elements such as carbon, silicon, manganese oxidation and nitriding to form various oxides and nitrides, and residual in the weld, resulting in slag inclusion or cracks in the weld. The gas in the weld pool may produce a large number of pores in the weld. These factors can greatly reduce the mechanical properties of the weld and make it brittle.