The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.

Different from the general zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach the former 6-8 times, so in the service life also has a great advantage, ordinary products three or five years began to corrosion and the latter will take longer to change. Stainless steel barbed rope is in the material aspect of protection, so the durability is also better, these two products are long in the service life, but in the price is high.

Galvanized iron wire is a substance we often see in life. It is the zinc gradually plated on the metal surface through the unidirectional current in the electroplating tank. The production speed is slow, the coating is uniform, the thickness is thin, usually only 3-15 microns, the appearance is bright, the corrosion resistance is poor, and the corrosion will rust in a few months. Galvanized wire has the characteristics of thick galvanized layer, strong corrosion resistance, strong galvanized layer, etc., the products are widely used in construction, highway walls, Zahua, weaving nets.

Large rolls of galvanized silk play a very important role in our life. Made of low carbon steel rod processing, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

Now large roll galvanized wire in our life the use of more and more, to galvanized wire products bring a great market, galvanized wire products are more and more types. The surface coating of good quality galvanized wire is continuous and smooth. When the plating parts are installed and combined, there can be no flow hanging, slag or drop remaining, and no surface defects such as iron exposure. Good quality galvanized wire, coating must be uniform, roughly uniform in copper sulfate solution soaking five times without exposing iron. And with hammering test does not bulge, do not fall off. This is a good galvanized wire should have characteristics.