The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Summer is the breeding season of mosquitoes, at this time, not only should pay attention to pet food and drinking water clean, but also pay attention to cleaning the dog cage regularly, so as to avoid pet disease.

To many people, a dog cage looks like a prison, but for dogs who have been raised on cage training, it is their home and shelter. A cage should be a comfortable place. Never put a dog in a cage for no reason. They will see it as punishment. (Why do many dogs fail to adapt to their owners’ commands, because whether the paparazzi can come out or not, it is also seen as a punishment.

Many people do not know how to choose high quality cut wire, I will give you a detailed introduction. The raw material of cutting wire is divided into: stainless steel cutting wire, copper cutting wire, steel wire cutting wire, copper plated steel wire cutting wire, galvanized steel wire cutting wire, iron wire cutting wire, aluminum wire cutting wire and so on.

The galvanized layer forms a particular metallurgical structure that is capable of accepting mechanical damage during transport and use. Every part of the plating can be zinc plated, even in dents, sharp corners and hidden places can be fully maintained. The galvanizing process is more convenient than other coating construction methods, and can avoid the required time after the installation on the site.

The electrode is a kind of material that the coating (that is, the coating) is uniformly and centrally applied on the welding core outside the metal welding core. The electrode is composed of two parts: the welding core and the coating. The welding core is the metal core of the electrode. In order to ensure the quality and performance of the weld, there are strict regulations on the content of various metal elements in the welding core. Electrode structure: portable non – electrode, including cylinder, tube, sleeve plug. The electrode is made of metal or metal oxide powder, such as high heat agent and additives. Paper tube is generally used for drug pipe, and metal tube can also be used for different welding parts and use environment. The plug is at the end of the electrode, which is the clamping part that matches the sleeve during welding and prevents the flux from leaking out of the tube.

The diameter of cold-drawn wire should conform to the contract, check whether the amount of zinc meets the requirements of the contract, check the tensile strength, and ask the factory to provide the corresponding inspection report. The wire factory introduces that the weight of a single coil of wire of different specifications should not be lower than the volume weight required by the contract, and record the value. No contacts are generated for each reel of wire. If there are contacts, no more than three contacts are generated for each reel. Each contact should be smooth surface treatment, the wire can not be pulled off from the contact, in line with customer packaging requirements.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.