Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.

3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag

Galvanized barbed wire as a safety protection of the metal wall, the galvanized barbed wire device also need to be protected for a long time? And how to protect it? Maintenance and protection of galvanized barbed rope. First, we can start from two aspects. One is about the protection of galvanized barbed rope posts.

This oxide film has greater elasticity and lubricity, does not affect the accuracy of parts. Therefore, the parts of precision instruments and optical instruments, spring steel, thin steel sheet, fine steel wire and so on are commonly bluing treatment. The commonly used galvanizing treatment of large roll galvanized wire is equivalent to forming a protective layer on the surface of the iron wire. The commonly used methods are hot dip galvanizing, hot spray plating, vacuum plating and so on. Different methods have corresponding characteristics.

4,  galvanized can be used zincate galvanized or chloride galvanized process, should use appropriate additives to meet the requirements of this standard coating.

As we all know, the mechanism of resistance to atmospheric corrosion of zinc includes mechanical protection and electrochemical protection. Under the condition of atmospheric corrosion, there are ZnO, Zn(OH)2 and basic zinc carbonate protective film on the surface of zinc layer, which to a certain extent slows the corrosion of zinc. When this protective film (also known as white rust) is damaged, a new film will be formed.

6, passivation to remove hydrogen parts should be passivation after the removal of hydrogen, passivation before the application of 1%H2SO4 or 1% hydrochloric acid activation 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.