Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.

Dog cage mainly by welding, spraying, injection molding, surface treatment, electroplating dog cage is made of high quality steel wire, dog cages are with plastic and plastic surface treatment, electrophoresis, chrome plating, galvanized, imitation gold, etc., according to the customer request processing, respectively, also can be customized to sample, dog cage assembly of compact structure, neat and beautiful appearance, make folding and remove the cage is more convenient and quick, won’t take up too much space.

Open pit coal mine due to poor air quality, a variety of harmful heavy metals are also more, so the corrosion strength of barbed rope products is particularly large, when using galvanized barbed rope must choose hot plating or plastic coated galvanized barbed rope, although the price is slightly higher, but in the long term development is more appropriate. Besides, when the barbed rope is installed near the coal mine, the pile foundation should be fixed to prevent the barbed rope from falling down due to soil erosion, thus losing the protective effect.

When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

Hexagonal twist flower network is divided into heavy hexagonal network and small hexagonal network two categories. Both are made of steel wire braided with various materials, the difference is that the former uses thicker steel wire, and the latter uses finer steel wire braided.

3. Put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and it is an important measure to stabilize the PH value in a numerical range. At the same time, it is convenient for the filter to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

Different from the general zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach the former 6-8 times, so in the service life also has a great advantage, ordinary products three or five years began to corrosion and the latter will take longer to change. Stainless steel barbed rope is in the material aspect of protection, so the durability is also better, these two products are long in the service life, but in the price is high.

Traditional wire mesh is crisscross woven into the wire, with the development of the economy, the rapid rise of all walks of life, the use of traditional wire mesh limitations gradually exposed, such as: aquaculture, to the chicken circle a cage can not be too dense, the wire can not be too thick, woven up the net wire once the mesh is too large net surface will become soft.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

Unless the stainless steel blade barbed rope is specially customized, it is usually produced by the mould with the knife length of 22mm, which is the BTO-22 type we usually call. This is not necessarily the specification from 11mm to 65mm are specifications. Unless the customer insists on customized length requirements, the barbed rope manufacturer will produce BTO-22 stainless steel blade barbed rope.

The cooling circulation system uses spray to cool the drawing die, and takes away a lot of heat generated by the drawing machine in high speed drawing in time to ensure the quality of the wire. Control drawing process parameters: drawing speed 10 ~ 12m/s; Winding tension 8 ~ 10N; Measuring length 30km; The mass fraction of lubricant is 3.5 ~ 4.5%; pH value of lubricant 7 ~ 8; Lubricant temperature 30 ~ 40℃.