The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Hot dip galvanizing is dipped in zinc liquid melted by heating. It has fast production speed, thick but uneven coating. The market thickness is 45g and can reach more than 300g. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

The production process of stainless steel blade and galvanized blade is basically similar. The blade size is usually determined according to the mold.

Cold plating is a physical treatment method, the zinc is simple and uneven, the amount of zinc is also less than in the corrosion and rust prevention and chemical disposal of hot plating; The amount of hot zinc plating is relatively thick, the surface of the disposal is flat on average, and it is not easy to fall off. A layer of alloy composed of zinc and metal has very strong oxidation ability, and there is a layer of pure zinc on the outside of this layer of alloy, which is why hot plating is thicker and stronger than cold plating. Under the condition of high degree of natural recovery, galvanized hook net can play a very good maintenance effect on the environment, it is not afraid of wind and rain, it is the battle machine in the hook net, much stronger than the dip plastic hook net.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

Large coil galvanized wire is made of high quality low carbon steel wire rod processing, is made of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling process and other processing. Galvanized wire is divided into hot galvanized wire and cold galvanized wire. Galvanized wire in the process of smelting there are a lot of need to pay more attention to the place, galvanized wire products in the manufacturing process will experience a lot of process, of which the following galvanized wire annealing is a very important step, this step to the nature of galvanized wire has brought a lot of help.

Titanium alloy with low carbon content is obtained because the carbon content remains the original concentration. The hardness of titanium alloy is mainly related to its carbon content. Therefore, after carburizing and subsequent heat treatment, the workpiece can obtain the performance of hard and tough inside. Galvanized wire varieties are mainly classified into three categories: electric galvanized wire, hot galvanized wire and galvanized wire. Among them, the classification of galvanized wire is divided into large roll galvanized wire, medium roll galvanized wire, small roll galvanized wire, galvanized shaft wire, truncated galvanized wire and other main production varieties.

Different supports are used for different installation environments. In the past, the blade barbed wire was not easy to fix, and the installation environment was often steep. Therefore, special tools must be used to fix the blade barbed wire to prevent it from being improperly installed.