There are three main factors affecting corrosion of stainless steel pet cages in Dalian:
Post time: 04-07-22In general, the cost of hot dipping zinc is lower than that of other maintenance coatings. The reason is very simple. Other maintenance coatings, such as sand painting, are labor-intensive processes, whereas hot dipping zinc processes are highly mechanized and tightly controlled in-plant construction. Hot dip zinc coating can be visually and briefly tested for non-destructive coating thickness.
- 3. Galvanizing: the preheated steel wire is immersed in the molten zinc liquid, so that the surface is attached with a zinc layer. The control of galvanizing time and temperature has great influence on the quality of zinc layer.
- The most obvious difference in a short time is the cross section of this piece, hot dip galvanized barbed wire because of surface anticorrosion treatment, so there will be rust in the cross section of this piece, and stainless steel barbed wire because the internal raw materials and surface raw materials are consistent, so there is no such situation.
Cleaning and disinfection methods of pet dog cage:
Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.
- 2.0*2.0mm 12 m/kg
If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.
- There are many blade specifications, first of all there are three types: spiral type, straight line, spiral cross type. Different units, the strength of the protection of different rope models. The blade barbed wire is mainly made of low carbon steel wire and aluminum magnesium alloy wire by spraying and welding. The blade material of the blade barbed wire is attached to the core wire made of stainless steel wire with professional mechanical strength, so the blade barbed wire has the advantages of good strength and aging resistance.
When a guided weight progress or repeated guided weight progress at a smaller height (driving) or left-handed and right-handed rope is used in pairs, ordinary wire rope can be selected. The determination of wire rope rotation should comply with: right-handed rope groove drum recommended use of left-handed wire rope: on the contrary, left-handed rope groove drum should use right-handed wire rope.
- With a large pickpocket for the steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for steel wire galvanized; Zinc pot steel wire outlet in 30 minutes, with the pickpocket back and forth, until the large, floating zinc residue into brown yellow, real zinc ash, zinc ash surface. The zinc ash taken out should be brown yellow real zinc ash, zinc surface, effectively reduce the zinc consumption. This is one of the biggest measures to reduce zinc consumption, and it is a real problem, which has not been solved for many years.
- 5, according to the wire diameter thickness to adjust zinc dipping time
The duration of the protective effect of galvanized layer on large roll galvanized wire is closely related to the coating thickness. Generally speaking, in the dry main gas and indoor use, the thickness of galvanized layer only 6-12μm, and in the environment is more severe conditions, galvanized layer thickness needs 20μm “to be up to 50μm”. Therefore, the influence of environment should be considered when choosing the thickness of galvanized layer.
Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.
Post time: 18-07-22- The installation of guardrail should also follow certain steps, first of all, after the guardrail is transported, according to the length of the guardrail, determine the distance between the column, if the installation of the guardrail field is soft ground, then you can first dig out a 40*40*50cm embedded machine base. If it is a concrete floor, as long as the expansion bolt directly fixed.
- 4. When cleaning the cage, remember not to brush violently, but pay attention to the strength. Otherwise easy to damage the surface of the paint layer.
- Three is to do a good job of galvanized silk product production site clean and tidy, in accordance with the scientific method of operation to operate the production, the operator should wear the required dress. If it is hot dip galvanized wire products, we must do a good job of passivation treatment, will be able to effectively prevent discoloration, prolong the method of discoloration, can solve the problem of discoloration.
Hot plating wire mixed rare earth and aluminum elements, make zinc liquid fluidity, more uniform coating, but also reduce zinc consumption. Hot-dip galvanized wire has better protective properties than cold galvanized wire, which makes it widely used in chemical experiment equipment. Hot plated wire coating is thick, so that it has good corrosion resistance, can be in the outdoor sun and rain and other harsh environment can be maintained for decades, so hot galvanized wire is widely used in construction, traffic guardrail and other outdoor facilities.
- For key and important parts with tensile strength greater than 1034Mpa, the stress should be removed at 200±10℃ for more than 1 hour before plating, and for carburized or surface hardened parts, the stress should be removed at 140±10℃ for more than 5 hours. The cleaning agent used for cleaning shall have no effect on the binding force of the coating and no corrosion on the substrate. Acid activation Acid activation solution should be able to remove corrosion products and oxide film (skin) on the surface of parts without excessive corrosion on the matrix.
- Positive twist: Twist two or more pieces of wire into a double wire rope and then wrap the wire around the double wire. It’s called a positive twist cord which is a common double strand cord.
Post time: 04-01-23The wire used for barbed wire is woven or welded with low carbon steel wire, medium carbon steel wire, high carbon steel wire, stainless steel wire and other materials. The production process includes: general braid, embossed braid and spot welding. If the material is steel wire, after equipment processing into a network, it is called wire mesh.