A. When the thickness of the plating is 3-4 mm, the zinc adhesion should be less than 460g/m, that is, the average thickness of the zinc layer is not less than 65 microns.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.

Poor pretreatment before plating; Bath temperature is too low; Poor quality of additives or too many additives and organic impurities will cause poor bonding. The quality of additives also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the crystal lattice and cause stress, causing the coating to bubble.

The production process of stainless steel blade and galvanized blade is basically similar. The blade size is usually determined according to the mold.

There is also a straight blade stabbing rope, which is mainly because the board and wire are not wound in the process of wrapping, so the blade stabbing rope produced is a straight product. The length of the barbed rope of this specification cannot be too long due to the limitation of logistics, and it cannot be bent because it is easy to be deformed by force. This is also the main reason why the barbed rope of the straight blade is not whole or long. Customers are advised to determine the spacing before purchase to prevent losses caused by no calculation.

Therefore, the rust of galvanized black iron wire has a great relationship with storage. At the same time, after rust, it is also necessary to conduct reasonable post-processing to avoid affecting its use effect. Of course, when the black iron wire is galvanized, it is also necessary to ensure the thickness of the galvanized layer, so that it can also reduce the possibility of rust. Speaking of galvanized iron wire, perhaps many people think it is relatively rare, in fact, it is not.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.

6, the use of special formula and special UV absorbent, no fading, no yellowing, no peeling, no cracking, no foaming, no moth, the use cycle can be more than 30 years.

The production process of stainless steel blade piercing rope is basically similar to that of galvanized blade piercing rope, and the blade size is usually determined according to the mold.