The skin of an adult person is, in most places, covered with a relatively thick (∼10 μm) barrier of keratinised dead cells. One of the main questions is still whether TiO₂ NPs are able to penetrate into the deeper layers of the skin. The majority of studies suggest that TiO₂ NPs, neither uncoated nor coated (SiO₂, Al₂O₃ and SiO₂/Al₂O₃) of different crystalline structures, penetrate normal animal or human skin. However, in most of these studies the exposures were short term (up to 48 h); only few long-term or repeated exposure studies have been published. Wu et al.83 have shown that dermal application of nano-TiO₂ of different crystal structures and sizes (4–90 nm) to pig ears for 30 days did not result in penetration of NPs beyond deep epidermis. On the other hand, in the same study the authors reported dermal penetration of TiO₂ NPs with subsequent appearance of lesions in multiple organs in hairless mice, that were dermal exposed to nano-TiO₂ for 60 days. However, the relevance of this study for human exposure is not conclusive because hairless mice skin has abnormal hair follicles, and mice stratum corneum has higher lipid content than human stratum corneum, which may contribute to different penetration. Recently Sadrieh et al. performed a 4 week dermal exposure to three different TiO₂ particles (uncoated submicron-sized, uncoated nano-sized and coated nano-sized) in 5 % sunscreen formulation with minipigs. They found elevated titanium levels in epidermis, dermis and in inguinal lymph nodes, but not in precapsular and submandibular lymph nodes and in liver. With the energy dispersive X-ray spectrometry and transmission electron microscopy (TEM) analysis the authors confirmed presence of few TiO₂ particles in dermis and calculated that uncoated nano-sized TiO₂ particles observed in dermis represented only 0.00008 % of the total applied amount of TiO₂ particles. Based on the same assumptions used by the authors in their calculations it can be calculated that the total number of particles applied was 1.8 × 10¹³ /cm² and of these 1.4 x10⁷/cm² penetrated. The surface area of skin in humans is around 1.8 m²  and for sun protection the cream is applied over whole body, which would mean that 4 week usage of such cream with 5 % TiO₂ would result in penetration of totally 2.6 × 10¹⁰ particles. Although Sadrieh et al.concluded that there was no significant penetration of TiO₂ NPs through intact normal epidermis, the results are not completely confirmative.

Food safety experts in the European Union (EU) have recently updated their safety assessment of TiO₂ as a food additive. In Europe, TiO₂ is referred to as E171, in accordance with European labelling requirements for food additives. The EU expert panel took into account toxicity studies of TiO₂ nanoparticles, which to this point had not been considered relevant to the safety assessment of TiO₂ as a food additive.  

After oral ingestion, the absorption of titanium dioxide particles is low, however they can accumulate in the body, Maged Younes, chair of the European Food Safety Authority's expert Panel on Food Additives and Flavourings, said in a May 2021 statement.

Relative Density Among commonly used white pigments, lithopone has the smallest relative density. Among white pigments of the same mass, titanium dioxide has the largest surface area and the highest pigment volume.

Historically, the first mentions of zinc sulfide being utilized as a pigment were approximately sixty years before the everyday use of lithopone. Originally, it was thought to be appropriate for coloring rubber. In England, a patent was granted for this process. Two decades after this, the focus shifted to zinc sulfide as a suitable pigment for paint. The year 1874 witnessed the patenting of a manufacturing process for a novel white pigment composed of zinc sulfide and barium sulfate. Dubbed Charlton white or Orr’s white enamel, this began a new era for white pigments.

The morphology of vitaminB2@P25TiO₂NPs is coherent with the description of Degussa P25 typical population. Size distribution histograms were made from manual measures of the nanoparticles observed in SEM micrographs using ImageJ®. This data showed that more than 70% is anatase (between 20 and 60 nm) with a minor amount of rutile characteristic bars (between 80 and 100 nm) and a small amount of amorphous phase (<40 nm) [36]. Further analysis of the same sample areas with an EDS probe demonstrated the presence of organic material composed of C and O (Fig. 2). This material was found homogeneously distributed on the surface of the different shapes of P25TiO₂NP, not in the background, indicating a specific interaction that could be attributed to the functionalization of the P25TiO₂NPs with vitamin B2.

Asia

Various titanium-rich minerals, including ilmenite and rutile, can serve as starting materials for the production of highly purified Titanium Dioxide. The predominant method employed in Titanium Dioxide production is the chloride process. In this process, the mineral, along with coke and chlorine, undergoes a reaction within a fluidized bed, resulting in the formation of primarily titanium tetrachloride and carbon dioxide. Subsequently, the titanium tetrachloride undergoes purification and conversion to Titanium Dioxide. Another method involves treating ilmenite with sulfuric acid to manufacture the chemical.

Lithopone