In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.

Spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and resistance to impact and oscillation. The strength and endurance objectives, especially to prevent the occurrence of modification cracks, are the key to the consumption of spring wire. The inner quality and outer quality of the wire rod directly affect the function of the wire.

Any application environment, users want a better the strength of the welded wire mesh, only need to improve its intensity, will make better the habit of using demand, but to be improved in the strength of this product, also need yo have a variety of conditions, will need to see factory in produce what kind of material, the strength of the product also is the material strength, But a manufacturer in the data does not fit the strength requirements, after all, there is no way to make the strength of the product progress, so this is the condition to.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

Some customers are more concerned about the quality of the problem, so for the service life is more important, thorn rope factory will generally recommend the use of high zinc thorn rope or stainless steel thorn rope.

Take 20cm galvanized wire for acid fog experiment, check the zinc content of galvanized wire through the balance to see whether it meets the zinc layer standard required by customers, ensure that the metal wire achieves the role of rust and corrosion prevention, and meet the service life required by customers. Galvanized iron wires must be packed in good condition, bound neatly and orderly, and bound inward to prevent scratches during transportation. The inspection standard of galvanized iron wire also includes the tensile test, which is decided according to the material of the galvanized wire order ordered by the customer, and it needs to be tested by comparing the raw material list.