3. Put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and it is an important measure to stabilize the PH value in a numerical range. At the same time, it is convenient for the filter to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

The size of the dog cage is generally relatively small, suitable for indoor small dogs, dog cage is easy to carry, go out to compare the use, folding dog cage high strength steel wire and steel pipe material, the outer layer spray treatment. Strong texture, excellent rust resistance, the dog cage inside the tray, can be pulled out, convenient to clean the dog’s urine and feces, folding, dog cage is suitable for families and pet stores to raise more pet dogs.

After electric galvanizing hot galvanizing. Electroplated copper and other common applications of screen consumption. The weaving of the binding of the building steel wire mesh has the first braided after plating, plating after weaving and other methods, after the disposal of the wire mesh or wire mesh has good corrosion, oxidation resistance characteristics, can be used in the construction, petroleum, chemical, aquaculture, garden protection, food processing and other industries of reinforcement, protection and insulation.

The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.

In daily life, what we can bend by hand is basically galvanized iron wire, not steel wire. It has a high zinc content, which ensures its good toughness and resilience, but also has ultra-high corrosion resistance, which can last for decades in outdoor environments. There are many practicability of galvanized iron wire, such as strong reliability, galvanized layer and iron together, form a special metallurgical structure, in the use and transportation process, can ensure that will not be mechanical damage.

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

Hexagonal mesh is a metal wire woven Angle mesh (hexagonal) made of wire mesh, the use of metal wire diameter is based on the size of the hexagonal and different. Also known as: twist flower net, stone cage net, gabion net, flood control network.

Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

For mountainous or hilly areas where the ground is more undulating set up stakes. You need to set a stake at the beginning and the end, and then determine the position. In the middle of the ups and downs, to increase the stakes according to the complexity of the ups and downs of the terrain, we need to be able to see 3 stakes at the same time, so that the installation is. It’s a straight line.