On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.

The barbed wire factory will store the blade barbed wire inventory in the appropriate place, because it understands the product characteristics.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

After proper heat treatment or cold drawing hardening, high carbon steel wire has high strength and hardness, high elastic limit and fatigue limit (especially notched fatigue limit), cutting function is acceptable, but welding function and cold plastic deformation ability is poor.

Annealed wire is a soft iron wire made of low carbon steel cold drawing, heating, constant temperature, heat preservation and other processes. The composition of iron wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet rolled into 6.5mm thick steel bar is the wire rod, and then put it into the wire drawing device into a different diameter of the line, and gradually reduce the aperture of the wire tray, cooling, annealing, plating and other processing technology made of various specifications of iron wire.