Hot dip galvanizing of steel plate is also called hot dip galvanizing. Zinc ingots are melted in the tropics and some auxiliary materials are added in hot dip galvanizing. The steel grid parts are then soaked in a galvanizing tank and a galvanizing layer is attached to the steel plate. The strength of hot dip galvanizing depends on its corrosion resistance, and the adhesion and hardness of galvanized sheet are better. The amount of galvanized steel plate after galvanizing. So this is the general amount of zinc.
Stainless steel barbed wire is mainly used in the place near the sea more, wet salty air for metal corrosion is particularly serious, and the selection of stainless steel barbed wire is in order to prevent corrosion.
Large roll galvanized wire is like the literal meaning, is wrapped in a layer of zinc on the surface of low carbon steel wire material, beautify the appearance at the same time, but also improve the corrosion resistance of galvanized wire. Zinc dissolves easily in acids and alkalis, so it is called a dissoluble metal. Zinc changes little in dry air. In moist air, a dense basic zinc carbonate film forms on the surface of zinc.
- The application range of small hexagonal mesh is also relatively wide, can be used for building wall fixed insulation layer, pipeline, boiler fixed heat preservation, decoration and other fields.
Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.
2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.
Traditional barbed wire is woven into wire, with the development of the economy, the rapid rise of all walks of life, the limitations of the use of traditional barbed wire gradually exposed, such as: aquaculture, to the chicken circle a cage can not be too dense, the wire can not be too thick, woven mesh wire once the mesh over the surface of the net will become soft. We also have the solutions: 1, rolling the straight wire into a wavy shape, but still not enough to feed chickens with mesh can only stretch out the chicken beak can not feed! 2, is electric welding mesh, with the current to the longitude and latitude of the wire spot welding together, mesh do more than most is not restricted.
- (7) twist twist hexagonal mesh is made to use low carbon steel wire galvanized large wire braided, the tensile strength of steel wire is not less than 38kg/㎡, the diameter of steel wire up to 2.0mm-3.2mm, the surface of steel wire is usually hot galvanized protection, galvanized protective layer thickness can be made according to customer requirements, galvanized amount can reach 300g/㎡.
So, do you know how to pick the right dog cage? When choosing a dog cage, focus on quality and practicality! Let’s take a look at it:
1. Electroplating process control
- The second is price.
Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.
- The key and important parts with tensile strength greater than 1034Mpa should be relieved of stress at 200±10℃ for more than 1 hour before plating, and the carburized or surface hardened parts should be relieved of stress at 140±10℃ for more than 5 hours. The cleaning agent used for cleaning shall have no effect on the binding force of the coating and no corrosion on the substrate. Acid activation Acid activation solution should be able to remove corrosion products and oxide film (skin) on the surface of parts without excessive corrosion on the matrix.
- Purpose of galvanized hexagonal net: building wall fixed, heat preservation, heat insulation; Power plant tied pipe, boiler warm; Anti-freezing, residential protection, landscaping protection; Raising chickens and ducks, isolating chicken and duck houses, to protect poultry; To protect and support seawalls, hillsides, roads and Bridges and other waterworks.
- And the role of wire mesh in the exterior wall plastering if from an Angle of anti-falling method, the effect of anti-cracking is relatively small, because of the azimuth problem; And about the external insulation system is used in the brick veneer, as for the role should also be anti-drop followed by anti-cracking, so we should choose the grid 10×10×0.6, these are some experience selection, the conversion of the grid comes from the national standards of steel wire mesh, the selection of steel content of the grade conversion.
- Two, the influence of steel wire surface roughness
- Galvanized hexagonal net is a galvanized metal wire mesh, the shape of the grid is hexagonal.
- In addition, the corrosion resistance of hot-dip galvanized wire will also be affected by other factors. For example, in different environments, especially in some special chemical environments, such as acidic or alkaline environments, the corrosion resistance of hot-dip galvanized wire may be affected to a certain extent. At this time, it may be necessary to use other materials that are more resistant to corrosion to replace the hot-dip galvanized wire.
Post time: 21-02-23Strength of galvanized wire: tensile strength is the great tensile stress that the material can withstand before tensile fracture; Yield strength has two indexes: upper yield and lower yield. It is a process in which the stress does not increase but the deformation continues to occur during the tensile process. When the force value drops for the first time, the major stress is the yield strength, and the yield strength must be less than the tensile strength.
- Galvanizing refers to the surface treatment technology of plating a layer of zinc on the surface of metal, alloy or other materials to play the role of aesthetics and rust prevention. The main method used now is hot galvanizing. However, hot dip galvanizing industry has been developed with the rapid development of cold strip rolling in the past 30 years. The production process of hot-galvanized sheet mainly includes: raw plate preparation → pre-plating treatment → hot-dip plating → post-plating treatment → finished product inspection and so on.