5, after the light plating should be carried out light treatment.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.

Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

Now it is mainly 12 or 14 galvanized barbed rope. Although they are calculated according to the price per ton, the calculation is different when it comes to every meter, because the thickness of the silk is not the same, which causes the problem that one galvanized barbed rope of equal weight is longer and the other is longer. Customers must have detailed communication with the barbed rope factory before purchasing to avoid such problems.

Large rolls of galvanized wire in oxygen violently extinguished, spark, and sodium block, magnesium strip in oxygen extinguished, no spark phenomenon. This phenomenon is determined by the composition of galvanized wire. The galvanized wire used in the experiment is pig iron or steel wire, pig iron and steel are iron and carbon alloy, containing iron and carbon two elements of complex material. Carbon in galvanized wire will produce carbon dioxide when extinguished, solid into gas, volume will shrink rapidly.

There is in place to use, the blade thorn rope is commonly border, installation and use of the fence, and prisons, and galvanized barbed wire is in the orchard, fence livestock and so on the installation of large area, although the use of relatively large, but not as good as the use of blade thorn rope and high grade, so this is also the main reason for the price is quite high. Finally, the general installation site of the blade barbed rope for the protection level requirements are relatively high, so the quality requirements for the product is also relatively high, but the ordinary galvanized barbed rope because of the requirements in the installation site is more casual, which is also for the processing process for the quality requirements are relatively low.