The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.
Different from the general zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach the former 6-8 times, so in the service life also has a great advantage, ordinary products three or five years began to corrosion and the latter will take longer to change. Stainless steel barbed rope is in the material aspect of protection, so the durability is also better, these two products are long in the service life, but in the price is high.
- Using the patented technology of the invention, regularly put zinc block into the plating aid pool, so that the bivalent iron in the plating aid into trivalent iron, and play a stable PH value in a numerical range of an important measure, but also easy to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.
- Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.
Stainless steel barbed wire in the way of corrosion is not too, because the surface is not treated but rely on its own raw materials for corrosion resistance, so there will be no chemical reaction.
- 6. If the damage volume of the bird cage is large, it needs to be repaired patiently. If the project is large, it needs to be repaired immediately to prevent the damage from continuing to expand. Of course, you can go to the repair shop to maintain specially.
Post time: 30-09-22Through the maintenance of galvanized wire, it can not only greatly prolong its service life, but also improve its efficiency in the daily use process. Because the labeled electrode potential of zinc is -0.762v, which is negative than iron, zinc becomes the anode when the galvanic cell is formed after being corroded by the medium. It itself is dissolved to protect the steel matrix. The duration of the protection of galvanized wire layer has a great relationship with the thickness.
In the thorn rope manufacturer, there are also great differences between hot galvanized thorn rope and cold galvanized thorn rope.
Electric galvanized wire is dipped in the zinc solution of heating ablation, the production speed is fast, the coating is thick but not uniform, the market allows a low thickness of 45 microns, up to 300 microns or more. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.
Post time: 08-06-22The reason why there are black spots in wire mesh welding is that the action of wire feeding should be timely filled in the melting time, and the development should be appropriate. There is no argon gas, long burning, large current, long distance, blunt tungsten needle and high molten pool temperature are the fundamental reasons for blackening. Continuous burning, is about active welding machine energy selection, machine welding will appear black spots.
- (2) Spray large number hook mesh guardrail should be used electric spray paint or electrostatic spray paint.
- Zinc pot workers should be determined to do duty and responsibility. Do not leave the post without leave, always observe the change of hot plating wire galvanized layer, and according to the analysis results, master the asbestos block gap friction, how long it takes to press, replace the pressing face; Adjust the working face; Until all four faces of the asbestos block are used up, maintenance workers can continue to use the asbestos block after repair when necessary to reduce the consumption of asbestos block.
Post time: 18-10-22
Post time: 02-08-22In addition, before the wire enters the zinc liquid, a layer of insulation material containing zinc oxide reducing agent can reduce the heat loss and zinc ash floating. When the zinc solution contains 0.002%-0.005% aluminum, the brightness of the zinc layer can be increased obviously, and excessive zinc ash can be prevented from oxidation on the surface of the zinc solution.
Post time: 10-05-23The decorative hook mesh is made of stainless steel, aluminum alloy, brass, red copper and other alloy materials by special technology. It is to do a good decorative screen, today we introduce the aperture and wire diameter of decorative hook mesh.
The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.