In view of this situation, many manufacturers are committed to ensuring the corrosion resistance of titanium and titanium alloy under the premise of increasing the hardness of titanium alloy, and surface carburizing is one of the typical processing technology means. Similar to the surface carburizing treatment of steel, the surface carburizing treatment of titanium alloy is to make the active carbon atoms, diffusion to the internal of titanium alloy, the formation of a certain thickness of higher carbon content of the carburizing layer, after quenching and tempering, so that the surface layer of the workpiece to obtain high carbon content of titanium alloy wire.

Spray hook net wholesale is the main component of hook net and frame, as for the frame is what kind of, can be customized according to requirements. Sometimes customers will purchase parts independently in order to reduce costs. In ORDER to ensure that spray hook net wholesale can be fixed on the ground, to ensure that its verticality to meet the requirements, it is necessary to hook net installation piling, fixed its guide frame, so that the installation of the net will achieve the requirements of use.

Cold wire drawing is a kind of cold processing of metal, that is, we often say reinforcement. Cold drawing process is not messy, cold drawing price based on the quality of cold drawing dividends of different levels, cold drawing production is also a variety of different procedures. The main factor affecting the strength of cold drawing wire is raw materials, which are closely related to the raw materials, strength and diameter of raw materials, and the better the quality of cold drawing wire, the more messy the production process.

Hot-dip galvanized wire is widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries. It has been widely used in recent years in agricultural fields such as agricultural medicine sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and so on.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.