Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

1, galvanized wire mesh molding sheet must be packed with flat hard data, to avoid eternal deformation due to poor packaging.

The physical methods mainly include manual rust removal and mechanical rust removal, chemical rust removal is generally the use of pickling method, practical application, usually according to the appearance of the workpiece rust status and different post-treatment process, choose different rust removal methods, among which pickling rust cleaning is more commonly used. That is, the iron and steel workpiece with oxide skin or rust is etched in the acid lotion, mainly to remove the oxide or rust layer on the surface of the steel.

The whole country is cooling down on a massive scale. People suddenly feel that winter is coming. In much of the north, the collection of central heating and heating also began. People who do not have central heating or do not want to use traditional heating choose air heating. As heating equipment enters the peak season, building network sales are also gradually increasing.

In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

The physical methods mainly include manual rust removal and mechanical rust removal, chemical rust removal is generally the use of pickling method, practical application, usually according to the appearance of the workpiece rust status and different post-treatment process, choose different rust removal methods, among which pickling rust cleaning is more commonly used. That is, the iron and steel workpiece with oxide skin or rust is etched in the acid lotion, mainly to remove the oxide or rust layer on the surface of the steel.

Blade barbed rope is a new product of safety protection supplies, and other barbed rope is different with very sharp blade, its production process is the stainless steel sheet stamping forming. The blade barbed wire protective net is a new kind of protective net. The blade barbed wire produced by our factory is made of corrosion-resistant hot-dip galvanized steel plate or stainless steel plate.

In the use of time do not need to carry out daily maintenance and maintenance, not only can save a lot of time, but also can reduce the cost, but also has good stability, strong corrosion resistance, greatly prolong the service life. According to the different process is divided into different kinds, can be selected according to their own needs, has good flexibility and elasticity. The main role of annealing wire is to control its degree of hardness and softness. When making annealing wire, it is made of steel wire.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.