2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

The production process is to roll the hot metal billet into 5mm thick steel, and then put it into the wire drawing device, draw into different diameters of the line and gradually reduce the aperture of the wire drawing disk. Production process through cooling, annealing, coating and other processing technology, and then made into a variety of different specifications of galvanized wire. Galvanized wire production because of simple process, wide application, early development. Galvanized wire or steel wire is a cold working product of steel wire, and the material used is generally low carbon steel or stainless steel.

There are still some differences between electric mesh and wire mesh and steel mesh. This mesh is mainly a welding mesh made of high quality low carbon steel wire after straightening and cutting, and then welded by electric welding equipment. It can be said that because of the characteristics of fast production and convenient transportation, it has been applied in many industries. In today’s construction projects, people can also see the image of this network well. The application of welded mesh in this industry is mentioned because of its strong corrosion resistance and uniform mesh. It has become a special grid for floor heating in construction industry and has been applied in many fields.

Steel mesh jinsu appearance treatment: polyethylene thermoplastic powder coatings is also called polyethylene powder coating, is the high pressure polyethylene (LDPE) as the basic material, adding a variety of function additives, colors, its antiseptic powder coating manufacturing processes, jinsu coating layer has the function of chemical, shock, circuitous, acid, salt fog corrosion, decorate a function and has good appearance.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

It is best to use special columns to fix the barbed rope installation, because the standard column is not only beautiful shape and better protection effect.

Many electrogalvanized wire diameter products are formed by wire drawing, wire drawing is a kind of processing technology, can make the product reach the required shape and meet the standard mechanical properties. Cold wire drawing is carried out at recrystallization temperature, hot wire drawing is carried out at crystallization temperature, warm wire drawing is drawn at higher than room temperature and lower than crystallization temperature. Cold drawing is a common drawing method.