Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

Now most people buy barbed rope choose blade barbed rope, why is this? The blade gill net is made of hot-dip galvanized steel plate or stainless steel sheet to punch out sharp knife sheets. The high tension galvanized steel wire or blade barbed wire is made of stainless steel wire as the core wire. Because the gill net shape is not easy to contact, so it can reach excellent protection barrier effect. The primary raw materials of the product are galvanized sheet and stainless steel plate.

Spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and resistance to impact and oscillation. The strength and endurance objectives, especially to prevent the occurrence of modification cracks, are the key to the consumption of spring wire. The inner quality and outer quality of the wire rod directly affect the function of the wire.

The production process is to roll the hot metal billet into 5mm thick steel, and then put it into the wire drawing device, draw into different diameters of the line and gradually reduce the aperture of the wire drawing disk. Production process through cooling, annealing, coating and other processing technology, and then made into a variety of different specifications of galvanized wire. Galvanized wire production because of simple process, wide application, early development. Galvanized wire or steel wire is a cold working product of steel wire, and the material used is generally low carbon steel or stainless steel.

In view of this situation, many manufacturers are committed to ensuring the corrosion resistance of titanium and titanium alloy under the premise of increasing the hardness of titanium alloy, and surface carburizing is one of the typical processing technology means. Similar to the surface carburizing treatment of steel, the surface carburizing treatment of titanium alloy is to make the active carbon atoms, diffusion to the internal of titanium alloy, the formation of a certain thickness of higher carbon content of the carburizing layer, after quenching and tempering, so that the surface layer of the workpiece to obtain high carbon content of titanium alloy wire.

Steel mesh galvanized: galvanized refers to the surface of metal, alloy or other materials coated with a layer of zinc to play a beautiful, rust prevention and other surface disposal technology. Now the first choice of method is hot dip galvanized, galvanized solution has cyanide bath and cyanide-free bath two categories. Cyanide bath bisects micro cyanide, low cyanide, medium cyanide, and high cyanide.